ProjectProducts have been widely used in steel, carbon, glass, cement, coking, building materials, non-ferrous and other industries, to meet the requirements of a variety of high-temperature furnace.
-
ProductsThe company's main products are clay bricks, high alumina bricks, dense clay bricks, magnesia carbon bricks, high-strength insulation bricks. Special products include sintered corundum brick, corundum mullite brick, chrome corundum brick, etc., as well as various amorphous refractory materials and various refractory clay.
-
AboutThe company started from refractory raw materials, in line with the business policy of integrity and win-win, customer first, relying on its own funds, rolling development, and has now developed into a modern refractory enterprise integrating scientific research, development, production and service.
-
NewsProducts sell well in 31 domestic provinces and autonomous regions, and exported to Southeast Asia and other countries
-
ContactIn case of product quality problems during the warranty period, we guarantee to deal with them in a timely manner. After the expiration of the warranty, we still provide after-sales service, only charge for materials. We promise to reply within 24 hours after receiving the call and arrive at the scene within 3 days.
- zzstgs@126.com
PROJECT CASE
Graphic Details
Reactive sintered silicon carbide rollers are suitable for high-temperature firing of roller kilns such as daily porcelain, sanitary porcelain, architectural porcelain, glass, and electromagnetic, lithium battery cathode and anode materials. The reaction sintered silicon carbide roller has a high temperature bearing capacity, no deformation after long-term use, and the service life is more than 10 times that of alumina ceramic rod.
General clay refractory mud
|
project |
Indicator parameters |
||||
|
NN-30 |
NN-38 |
NN-42 |
NN-45 |
||
|
Al2O3,% is not less than |
30 |
38 |
42 |
45 |
|
|
Refractoriness, °C not lower |
1620 |
1680 |
1700 |
1720 |
|
|
Flexural strength at room temperature, MPa |
After drying at 110 °C, ≮ |
1.0 |
1.0 |
1.0 |
1.0 |
|
After burning at 1200°C*3h, ≮ |
3.0 |
3.0 |
3.0 |
3.0 |
|
|
Heating permanent line change rate, % 1200 °C * 3 hours after burning |
-5~+1 |
||||
|
Bonding time, min |
1~3 |
||||
|
Granularity, % |
＜1.0mm |
100 |
|||
|
>0.5mm is not greater than |
2 |
||||
|
< 0.075mm is not less than |
50 |
||||
Service
Official website orders are shipped by the headquarters.
Spot payment after 3-15 working days issued, no spot normal 25 working days issued.
If the goods cannot meet the ordinary mode of transportation, please inform in advance of other circumstances and settle through negotiation.
顺通耐材
Address: Pingmo Town, Xinmi City, Henan Province
Telephone:0086371-85811678
E-mail: zzstgs@126.com
Copyright©2024 Zhengzhou Shuntong New Refractory Co., Ltd.